Alumina Carrier Columnar (clover shape)

Posted on by

This series of products with false water alumina gel X- Rhoactivated alumina production fast removal method and continuouscarbonization method for the production of components, made ofadvanced molding technology, high specific surface area, goodstability of compressive strength, low abrasion, proper pore structure, low content of impurities, the characteristics of active component impregnation properties good etc.,
and according to user requirements, using different process conditions, catalyst carrierto adjust the production performance of materialized different crystal phases, different diameter, different content of impurities.Widely used in petrochemical, hydrodesulfurization, low temperature shift catalyst carrier.
The main product type and technical indicator:
The content of *Na2O according to user needs

rType        Component Appearance Size
mm		 Bulk Density
g/cm3		 BETm2/g Pole Volum
cm3/g		 Crush stength

N/Grain

 Na2O % Al2O3 % Water adsorption%
HYZ-001 Al2O3•nH2O Column 3×(4-10) 0.55-0.65 ≥150 ≥0.50 ≥100 ≤0.10 ≥94 ≥70
HYZ-002 Al2O3•nH2O clover 3×(4-10) 0.55-0.65 ≥150 ≥0.50 ≥100 ≤0.10 ≥94 ≥70
HYZ-003 Al2O3•nH2O Column 3×(4-10) 0.5-0.6 ≥220 ≥0.60 ≥90 ≤0.10 ≥94 ≥70
HYZ-004 Al2O3•nH2O clover 3×(4-10) 0.5-0.6 ≥220 ≥0.60 ≥90 ≤0.10 ≥94 ≥70
HYZ-005 Silicon aluminum composite Column 3×(4-10) 0.5-0.6 ≥180 ≥0.50 ≥100 ≤0.10 ≥84 ≥65
HYZ-006 Silicon aluminum composite Clover 3×(4-10) 0.5-0.6 ≥180 ≥0.50 ≥100 ≤0.10 ≥84 ≥65
HYZ-007 Titaniumaluminum composite  Column 3×(4-10) 0.55-0.65 ≥150 ≥0.45 ≥90 ≤0.15 ≥84 ≥72
HYZ-008 Titaniumaluminum composite Column 3×(4-10) 0.55-0.65 ≥150 ≥0.45 ≥90 ≤0.15 ≥84 ≥72
HYZ-009 Al2O3•nH2O Column 3×(4-10) 0.70-0.80 ≥180 ≥0.40 ≥80 ≤0.10 ≥94 ≥50
HYZ-010 Al2O3•nH2O Sphere Φ3-4 ≥0.68 ≥170 ≥0.45 ≥70 ≤0.20 ≥94 ≥65
HYZ-011 Al2O3•nH2O Sphere Φ5-7 ≥0.68 ≥170 ≥0.45 ≥130 ≤0.25 ≥94 ≥50
HYZ-012 Al2O3•nH2O Sphere Φ4-6 0.55-0.60 ≥250 ≥0.45 ≥60 0.10-1.00 ≥94 ≥60-70
HYZ-013 Al2O3•nH2O Clover 3×(4-10) 0.45-0.60 ≥350 ≥0.65 ≥70 ≤0.10 ≥95 ≥80